Poliuretano elastomeroa hautatzeko moldaketa prozesatzeko oinarrizko oinarriak

Ren oinarrizko printzipioakpoliuretanoaelastomeroa hautatzeko moldaketa prozesatzeko metodoa

Poliuretanoa elastomer formed by the polymerization reaction of diisocyanate and active hydrogen compound, the rigid segment containing urea group composed of diisocyanate and diamine chain extender, the glass transition temperature is much higher than room temperature, and it is glassy at room temperature. Subcrystals or microcrystals form the plastic phase; flexible segments of polyether or polyester are gathered together to form the matrix or matrix of the poliuretanoa rubber. Because its glass transition temperature is lower than room temperature, it is called the rubber phase. The microphase separation of the poliuretanoa elastomer makes the poliuretanoa elastomer have the advantages of good wear resistance, wide range of hardness, high strength and high elongation, large load supporting capacity, good shock absorption effect and excellent oil resistance. Choosing a suitable molding and processing method can maximize the performance of poliuretanoa elastomers and prepare various poliuretanoa elastomers with excellent properties, which are widely used as plastics, rubber, fibers, adhesives and coatings, and even as functional polymer materials. Such as medical poliuretanoamaterialak.

1.1 Konformatzeko prozesatzeko metodoak hautatzeko printzipio orokorrak

(1) Moldeatze prozesua normalean konposatu polimerikoa egoera solidoan (hautsa edo granularra), itsatsi edo disoluzio egoeran urtu edo deformatzea da, eta nahi den forma molde baten bidez eratzea eta lortutako forma mantentzea eta azkenean lortzea produktua. artisautza prozesua.

(2) Moldeatze prozesuaren fluxu arrunta: â ‘Polimero konposatu nahasketa behin eta bitan produktuak ekoizteko eratzeko metodoa; â‘¡Polimero konposatua osatzeko metodoa aldi berean produktuak ekoizteko; â ‘¢ Monomero nahasketatik produktuak pauso batean ekoizteko metodoa â’ £ Oligomero nahasketaren urrats bateko produkzio metodoa.

(3) Prozesamenduaren errendimendua eta eragiteko faktoreak: â ‘Estutzeko modua, estrusorean, injekzio-makinaren upelean, egutegiaren arraboletan eta moldean, materiala estrusioaren bidez deformatzen denean, materialaren forma lortzen da. eta gaitasuna mantendu. Faktore murriztaileak: urtutako biskositatea, prozesatzeko ekipoen egitura, urtutako erreologia eta urtutako emaria. â‘¡Moldagarritasuna, injekzio makinaren, estrusioaren eta konpresio makinaren eraginez moldeatzeko prozesuan materiala tenperatura eta presioaren eta moldean moldatzeko gaitasunaren pean deformatzen da. Faktore murriztaileak: erreologia, propietate termikoak eta beste propietate fisiko eta mekaniko batzuk eta polimero konposatuen erreaktibitate kimikoa. â ‘¢ Luzagarritasuna, egutegietan edo luzatzean, materiala deformatu egiten da egutegia edo norabide batean edo bitan luzatuz. Faktore murriztaileak: materialaren plastizitatea eta tentsio gogortze efektua. â '£ Spinnability, pita estrusioaren moldaketa bitartean, materialak moldearen bidez zuntz solido jarraiak eratzeko duen ahalmena. Faktore murriztaileak: erreologia, urtutako biskositatea eta erresistentzia, egonkortasun termikoa eta egonkortasun kimikoa.

1.2 Moldatzeko eta prozesatzeko metodoak hautatzeko printzipio orokorrakpoliuretanoaelastomeroak

Poliuretanoa elastomer molding processing system is divided into liquid system and solid system. On the basis of the rapid polymerization reaction of diisocyanate and active hydrogen compound, the molding processing method is conducive to the microphase separation of the poliuretanoa elastomer. , Liquid system, poliuretanoa casting glue can be processed by casting (manual casting, centrifugal casting and vacuum casting), reaction injection molding, spraying, knife coating, roller coating, laminating, laminating, bonding, vulcanizing, pasting and rubbing ; Solid system, poliuretanoa compound rubber can be vulcanized and laminated with mold, poliuretanoa thermoplastic can be used with thermoplastic, hot injection, calendering, blow molding, spinning and lamination.

1.3 Oinarrizko moten eta moldaketa prozesatzeko metodoen bat etortzeko printzipioa

Poliuretanoaelastomeroa plastikoaren eta kautxuaren arteko polimero altua da bere moduluari dagokionez. Batez ere biltzen ditupoliuretanoa compound rubber, poliuretanoa cast rubber, poliuretanoa water emulsion and poliuretanoa thermoplastic. Poliuretanoa leather, poliuretanoa adhesives, poliuretanoa coatings, poliuretanoa compounds, poliuretanoa casting glues, poliuretanoa fibers, poliuretanoa water emulsions and poliuretanoa thermoplastics are all derived from the above four types of glue. The molding and processing methods of poliuretanoa compound rubber, poliuretanoa water emulsion and poliuretanoa thermoplastic generally belong to the molding processing methods of rubber, coatings and plastics.

1.4 The use of poliuretanoa elastomers and the matching principle of production continuity and molding processing methods

Poliuretanoa elastomer molding and processing methods are matched with the use of poliuretanoa elastomers, taking into account the continuity of production. For example, poliuretanoa leather molding methods usually use poliuretanoa casting adhesive or foaming layer, poliuretanoa water emulsion and poliuretanoa thermoplastic as the surface layer; also available Poliuretanoa thermoplastic and poliuretanoa water emulsion are used as leather separately, which are based on the basic rubber molding processing method, supplemented by foam molding processing, usually calender molding processing method is selected. Poliuretanoa paving materials are made of poliuretanoa casting glue, mainly due to the large product shape and low precision requirements. Medical poliuretanoa materials have good chemical stability, tissue compatibility, and resistance to biological aging, so the molding process uses dip coating, pouring and coating methods.